Cu-Mg-O thin films by RF magnetron co-sputtering: Their band offsets with CdS in heterojunction solar cells
We report on Cu-Mg.O thin films of 100 - 300 nm in thickness produced by radio frequency (RF) reactive sputtering fromCu and Mg-metal targets in an argon-oxygen ambient. The amount of Mg in the thin films was varied through changingthe RF power applied at the Mg target. When the Mg content in the Cu...
| Autores principales: | , , , |
|---|---|
| Formato: | Artículo |
| Lenguaje: | español |
| Publicado: |
Universidad Autónoma de Nuevo León
2022
|
| Materias: | |
| Acceso en línea: | https://quimicahoy.uanl.mx/index.php/r/article/view/298 |
| Sumario: | We report on Cu-Mg.O thin films of 100 - 300 nm in thickness produced by radio frequency (RF) reactive sputtering fromCu and Mg-metal targets in an argon-oxygen ambient. The amount of Mg in the thin films was varied through changingthe RF power applied at the Mg target. When the Mg content in the Cu-Mg-O film changed from 0 to 0.3, the opticalbandgap increased from 1.73 eV to 2.13 eV, and the electrical conductivity decreased from 9 x 10-3 Ω-1 cm-1(CuxO) to 6.7x 10-5 Ω-1 cm-1(Cuo7/Mg0.30). Solar cells of these films, FTO/ CdS/Cu0.85Mg0.15O/C-Ag, showed a short circuit current density of 2.86 mA/cm2 an open circuit voltage of 378 mV, and power conversion efficiency of 0.25%. X-ray photo-electron spectroscopy depth profile analyses of the interfaces suggest a negative conduction band offset in CdS/Cu0.85Mg0.15O( — 0.74 eV) as well as in CdS/CuxO (0.9 eV) solar cells. |
|---|---|
| Descripción Física: | Quimica Hoy; Vol. 11 No. 03 (2022): Julio-septiembre 2022; 41-49 Quimica Hoy; Vol. 11 Núm. 03 (2022): Julio-septiembre 2022; 41-49 2007-1183 |