Microwave-assisted synthesis and characterization of microstar shaped zinc oxide

A microwave-assisted solution-phase approach has been applied for the synthesis ofzinc oxide microstructures. Toe synthesis procedure was carried out by using the reagents: Zinc ni trate and Methenamine, at stoichiometric ratio. Analysis by means ofX-ray Diffraction (XRD) shows a crystalline phase i...

Descripción completa

Detalles Bibliográficos
Autores principales: Gómez, Idalia, Yucam´án, Miguel José, Palomar, Flor
Formato: Artículo
Lenguaje:inglés
Publicado: Universidad Autónoma de Nuevo León 2012
Materias:
Acceso en línea:https://quimicahoy.uanl.mx/index.php/r/article/view/152
Descripción
Sumario:A microwave-assisted solution-phase approach has been applied for the synthesis ofzinc oxide microstructures. Toe synthesis procedure was carried out by using the reagents: Zinc ni trate and Methenamine, at stoichiometric ratio. Analysis by means ofX-ray Diffraction (XRD) shows a crystalline phase in hexagonal wurtzite arrangement for ZnO. The presence ofmicrostar shaped zinc oxide (2-3μm) with nanorods,f50nm) arranged has been confirmed from High Resolution Scanning Electron Microscopy (HRSEM). The formation of nanorods was confirmed by Transmission Electron Microscopy. In Raman spectroscopy a red shift was detected in the microstructures compared with ZnO bulk. High crystalline materials without additional post-synthesis treatrnent were found.