Estudio del comportamiento a fatiga a bajo ciclo de las aleaciones de aluminio hipoeutécticas por Aguilar Navarro, Jorge Alberto

“…On the other hand, the crack propagation phenomenon was caused by the coalescence of microcracks, through regions with a higher density of defects and brittle particles, until they grew into macroscopic cracks and, finally, presenting a ductile fracture mode Coalescence, that is, the union and interaction between micropores, accelerated the fracture. …”
Enlace del recurso

Estudio del comportamiento a fatiga a bajo ciclo de las aleaciones de aluminio hipoeutécticas por Aguilar Navarro, Jorge Alberto

“…On the other hand, the crack propagation phenomenon was caused by the coalescence of microcracks, through regions with a higher density of defects and brittle particles, until they grew into macroscopic cracks and, finally, presenting a ductile fracture mode Coalescence, that is, the union and interaction between micropores, accelerated the fracture. …”