Effect of water on the stress corrosion cracking behavior of API 5L-X52 Steel in E95 Blend
The effect of water content (0.5%, 1%, 2%, 5%, 10% y 20 V%) in E95 blend (5 V% gasoline – 95 V% ethanol) on the stress corrosion cracking (SCC) susceptibility of X-52 carbon steel was investigated. Slow strain rate tests (SSRT) coupled with electrochemical noise measurements (ECN) were carried out u...