Corrosion resistance of aluminum alloy AA2024 with hard anodizing in sulfuric acid-free solution
In the aeronautical industry, Al-Cu alloys are used as a structural material in the manufacturing of commercial aircraft due to their high mechanical properties and low density. One of the main issues with these Al-Cu alloy systems is their low corrosion resistance in aggressive substances; as a res...
| Autores principales: | , , , , , , , , , , |
|---|---|
| Formato: | Artículo |
| Lenguaje: | inglés |
| Publicado: |
Molecular Diversity Preservation International
2022
|
| Materias: | |
| Acceso en línea: | http://eprints.uanl.mx/24980/1/materials-15-06401.pdf |
| _version_ | 1824420049825300480 |
|---|---|
| author | Cabral Miramontes, José Ángel Gaona Tiburcio, Citlalli García Mata, Estefanía Esneider Alcála, Miguel Ángel Maldonado Bandala, Erick Lara Banda, María del Refugio Nieves Mendoza, Demetrio Olguín Coca, Javier Zambrano Robledo, Patricia del Carmen López León, Luis Daimir Almeraya Calderón, Facundo |
| author_facet | Cabral Miramontes, José Ángel Gaona Tiburcio, Citlalli García Mata, Estefanía Esneider Alcála, Miguel Ángel Maldonado Bandala, Erick Lara Banda, María del Refugio Nieves Mendoza, Demetrio Olguín Coca, Javier Zambrano Robledo, Patricia del Carmen López León, Luis Daimir Almeraya Calderón, Facundo |
| author_sort | Cabral Miramontes, José Ángel |
| collection | Repositorio Institucional |
| description | In the aeronautical industry, Al-Cu alloys are used as a structural material in the manufacturing of commercial aircraft due to their high mechanical properties and low density. One of the main issues with these Al-Cu alloy systems is their low corrosion resistance in aggressive substances; as a result, Al-Cu alloys are electrochemically treated by anodizing processes to increase their corrosion resistance. Hard anodizing realized on AA2024 was performed in citric and sulfuric acid solutions for 60 min with constant stirring using current densities 3 and 4.5 A/dm2. After anodizing, a 60 min sealing procedure in water at 95 °C was performed. Scanning electron microscopy (SEM) and Vickers microhardness (HV) measurements were used to characterize the microstructure and mechanical properties of the hard anodizing material. Electrochemical corrosion was carried out using cyclic potentiodynamic polarization curves (CPP) and electrochemical impedance spectroscopy (EIS) in a 3.5 wt. % NaCl solution. The results indicate that the corrosion resistance of Al-Cu alloys in citric acid solutions with a current density 4.5 A/dm2 was the best, with corrosion current densities of 2 × 10−8 and 2 × 10−9 A/cm2. Citric acid-anodized samples had a higher corrosion resistance than un-anodized materials, making citric acid a viable alternative for fabricating hard-anodized Al-Cu alloys. |
| format | Article |
| id | eprints-24980 |
| institution | UANL |
| language | English |
| publishDate | 2022 |
| publisher | Molecular Diversity Preservation International |
| record_format | eprints |
| spelling | eprints-249802024-02-28T15:25:25Z http://eprints.uanl.mx/24980/ Corrosion resistance of aluminum alloy AA2024 with hard anodizing in sulfuric acid-free solution Cabral Miramontes, José Ángel Gaona Tiburcio, Citlalli García Mata, Estefanía Esneider Alcála, Miguel Ángel Maldonado Bandala, Erick Lara Banda, María del Refugio Nieves Mendoza, Demetrio Olguín Coca, Javier Zambrano Robledo, Patricia del Carmen López León, Luis Daimir Almeraya Calderón, Facundo Ingeniería y Tecnología TA Ingeniería General y Civil In the aeronautical industry, Al-Cu alloys are used as a structural material in the manufacturing of commercial aircraft due to their high mechanical properties and low density. One of the main issues with these Al-Cu alloy systems is their low corrosion resistance in aggressive substances; as a result, Al-Cu alloys are electrochemically treated by anodizing processes to increase their corrosion resistance. Hard anodizing realized on AA2024 was performed in citric and sulfuric acid solutions for 60 min with constant stirring using current densities 3 and 4.5 A/dm2. After anodizing, a 60 min sealing procedure in water at 95 °C was performed. Scanning electron microscopy (SEM) and Vickers microhardness (HV) measurements were used to characterize the microstructure and mechanical properties of the hard anodizing material. Electrochemical corrosion was carried out using cyclic potentiodynamic polarization curves (CPP) and electrochemical impedance spectroscopy (EIS) in a 3.5 wt. % NaCl solution. The results indicate that the corrosion resistance of Al-Cu alloys in citric acid solutions with a current density 4.5 A/dm2 was the best, with corrosion current densities of 2 × 10−8 and 2 × 10−9 A/cm2. Citric acid-anodized samples had a higher corrosion resistance than un-anodized materials, making citric acid a viable alternative for fabricating hard-anodized Al-Cu alloys. Molecular Diversity Preservation International 2022-09-15 Article PeerReviewed text en cc_by_nc_nd http://eprints.uanl.mx/24980/1/materials-15-06401.pdf http://eprints.uanl.mx/24980/1.haspreviewThumbnailVersion/materials-15-06401.pdf Cabral Miramontes, José Ángel y Gaona Tiburcio, Citlalli y García Mata, Estefanía y Esneider Alcála, Miguel Ángel y Maldonado Bandala, Erick y Lara Banda, María del Refugio y Nieves Mendoza, Demetrio y Olguín Coca, Javier y Zambrano Robledo, Patricia del Carmen y López León, Luis Daimir y Almeraya Calderón, Facundo (2022) Corrosion resistance of aluminum alloy AA2024 with hard anodizing in sulfuric acid-free solution. Materials, 15 (18). pp. 1-21. ISSN 1996-1944 https://doi.org/10.3390/ma15186401 https://doi: 10.3390/ma15186401 |
| spellingShingle | Ingeniería y Tecnología TA Ingeniería General y Civil Cabral Miramontes, José Ángel Gaona Tiburcio, Citlalli García Mata, Estefanía Esneider Alcála, Miguel Ángel Maldonado Bandala, Erick Lara Banda, María del Refugio Nieves Mendoza, Demetrio Olguín Coca, Javier Zambrano Robledo, Patricia del Carmen López León, Luis Daimir Almeraya Calderón, Facundo Corrosion resistance of aluminum alloy AA2024 with hard anodizing in sulfuric acid-free solution |
| thumbnail | https://rediab.uanl.mx/themes/sandal5/images/online.png |
| title | Corrosion resistance of aluminum alloy AA2024 with hard anodizing in sulfuric acid-free solution |
| title_full | Corrosion resistance of aluminum alloy AA2024 with hard anodizing in sulfuric acid-free solution |
| title_fullStr | Corrosion resistance of aluminum alloy AA2024 with hard anodizing in sulfuric acid-free solution |
| title_full_unstemmed | Corrosion resistance of aluminum alloy AA2024 with hard anodizing in sulfuric acid-free solution |
| title_short | Corrosion resistance of aluminum alloy AA2024 with hard anodizing in sulfuric acid-free solution |
| title_sort | corrosion resistance of aluminum alloy aa2024 with hard anodizing in sulfuric acid free solution |
| topic | Ingeniería y Tecnología TA Ingeniería General y Civil |
| url | http://eprints.uanl.mx/24980/1/materials-15-06401.pdf |
| work_keys_str_mv | AT cabralmiramontesjoseangel corrosionresistanceofaluminumalloyaa2024withhardanodizinginsulfuricacidfreesolution AT gaonatiburciocitlalli corrosionresistanceofaluminumalloyaa2024withhardanodizinginsulfuricacidfreesolution AT garciamataestefania corrosionresistanceofaluminumalloyaa2024withhardanodizinginsulfuricacidfreesolution AT esneideralcalamiguelangel corrosionresistanceofaluminumalloyaa2024withhardanodizinginsulfuricacidfreesolution AT maldonadobandalaerick corrosionresistanceofaluminumalloyaa2024withhardanodizinginsulfuricacidfreesolution AT larabandamariadelrefugio corrosionresistanceofaluminumalloyaa2024withhardanodizinginsulfuricacidfreesolution AT nievesmendozademetrio corrosionresistanceofaluminumalloyaa2024withhardanodizinginsulfuricacidfreesolution AT olguincocajavier corrosionresistanceofaluminumalloyaa2024withhardanodizinginsulfuricacidfreesolution AT zambranorobledopatriciadelcarmen corrosionresistanceofaluminumalloyaa2024withhardanodizinginsulfuricacidfreesolution AT lopezleonluisdaimir corrosionresistanceofaluminumalloyaa2024withhardanodizinginsulfuricacidfreesolution AT almerayacalderonfacundo corrosionresistanceofaluminumalloyaa2024withhardanodizinginsulfuricacidfreesolution |