Failure analysis of Co–Cr hip resurfacing prosthesis during solidification
In this study a failure originated during solidification process into the femoral stem component of Hip Resurfacing prosthesis was investigated. Visual inspection, optical microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and a commercial software simulation Pro...
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
2013
|
| Online Access: | http://eprints.uanl.mx/14905/1/546.pdf |
| _version_ | 1824414182795116544 |
|---|---|
| author | Alvarez Vera, Melvyn García Duarte, José Hilario Juárez Hernández, Arturo Mercado Solis, Rafael David Castillo, A. G. Hernández Rodríguez, Marco Antonio Loudovic |
| author_facet | Alvarez Vera, Melvyn García Duarte, José Hilario Juárez Hernández, Arturo Mercado Solis, Rafael David Castillo, A. G. Hernández Rodríguez, Marco Antonio Loudovic |
| author_sort | Alvarez Vera, Melvyn |
| collection | Repositorio Institucional |
| description | In this study a failure originated during solidification process into the femoral stem
component of Hip Resurfacing prosthesis was investigated. Visual inspection, optical
microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS)
and a commercial software simulation ProCAST were carried out in order to determine the
cause and solution of this failure. The results exhibited hot tearing, shrinkage porosity and
metal oxide films due to inadequate heat dissipation during solidification process, as a
consequence of poor investment casting ceramic mold configuration. Also in this paper
was improved the casting design solving this kind of defects. |
| format | Article |
| id | eprints-14905 |
| institution | UANL |
| language | English |
| publishDate | 2013 |
| record_format | eprints |
| spelling | eprints-149052024-03-05T17:36:51Z http://eprints.uanl.mx/14905/ Failure analysis of Co–Cr hip resurfacing prosthesis during solidification Alvarez Vera, Melvyn García Duarte, José Hilario Juárez Hernández, Arturo Mercado Solis, Rafael David Castillo, A. G. Hernández Rodríguez, Marco Antonio Loudovic In this study a failure originated during solidification process into the femoral stem component of Hip Resurfacing prosthesis was investigated. Visual inspection, optical microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and a commercial software simulation ProCAST were carried out in order to determine the cause and solution of this failure. The results exhibited hot tearing, shrinkage porosity and metal oxide films due to inadequate heat dissipation during solidification process, as a consequence of poor investment casting ceramic mold configuration. Also in this paper was improved the casting design solving this kind of defects. 2013 Article PeerReviewed text en cc_by_nc_nd http://eprints.uanl.mx/14905/1/546.pdf http://eprints.uanl.mx/14905/1.haspreviewThumbnailVersion/546.pdf Alvarez Vera, Melvyn y García Duarte, José Hilario y Juárez Hernández, Arturo y Mercado Solis, Rafael David y Castillo, A. G. y Hernández Rodríguez, Marco Antonio Loudovic (2013) Failure analysis of Co–Cr hip resurfacing prosthesis during solidification. Case studies in engineering failure analysis, 1 (1). pp. 1-5. ISSN 2213-2902 http://doi.org/10.1016/j.csefa.2012.10.002 doi:10.1016/j.csefa.2012.10.002 |
| spellingShingle | Alvarez Vera, Melvyn García Duarte, José Hilario Juárez Hernández, Arturo Mercado Solis, Rafael David Castillo, A. G. Hernández Rodríguez, Marco Antonio Loudovic Failure analysis of Co–Cr hip resurfacing prosthesis during solidification |
| thumbnail | https://rediab.uanl.mx/themes/sandal5/images/online.png |
| title | Failure analysis of Co–Cr hip resurfacing prosthesis during solidification |
| title_full | Failure analysis of Co–Cr hip resurfacing prosthesis during solidification |
| title_fullStr | Failure analysis of Co–Cr hip resurfacing prosthesis during solidification |
| title_full_unstemmed | Failure analysis of Co–Cr hip resurfacing prosthesis during solidification |
| title_short | Failure analysis of Co–Cr hip resurfacing prosthesis during solidification |
| title_sort | failure analysis of co cr hip resurfacing prosthesis during solidification |
| url | http://eprints.uanl.mx/14905/1/546.pdf |
| work_keys_str_mv | AT alvarezveramelvyn failureanalysisofcocrhipresurfacingprosthesisduringsolidification AT garciaduartejosehilario failureanalysisofcocrhipresurfacingprosthesisduringsolidification AT juarezhernandezarturo failureanalysisofcocrhipresurfacingprosthesisduringsolidification AT mercadosolisrafaeldavid failureanalysisofcocrhipresurfacingprosthesisduringsolidification AT castilloag failureanalysisofcocrhipresurfacingprosthesisduringsolidification AT hernandezrodriguezmarcoantonioloudovic failureanalysisofcocrhipresurfacingprosthesisduringsolidification |